The AC-JIII Self-leveling Refractory Deck Covering

产品介绍： 1、Type of construction Use for the A-60 deck system(see A-60 deck specification) 2、Technical Index Serial NumberProject NameTechnical Index1Dry Density≤1700kg/m3Density≤1900kg/m32· Fluidity Φ≥130mm3Breaking Strength ≥3.5MPa4Compressive Strength≥10MPa5· Water Absorption ≤10％6· oil absorption ≤5%7Heat Conductivity Coefficient ≤1.2W/(m.K)8Impact ResistanceNo crack, no shell9Initial Setting Time≥1h10· Final Setting Time ≤8h11Vibratory TestNo crack, no shell12Organic Content≤10％13NoninflammabilityComply with IMO 2010 FTP Code Part 1 3、The performance characteristics This product is non-toxic, strong adhesion, low thermal conductivity, good liquidity, impact resistant, wear resistant, products forming smooth,sound insulation is strong, curing time steady, etc.Its construction technology is simple and apply to the A60 refractory deck area of the vessel . 4、Fire resistance rating Noninflammability: comply with IMO 2010 FTP Code Part 1. 5、Recognised classification society DNV.GL、CCS、EC 6、Packaging and dosage Package:25KG/bag 40bags/pallet Dosage:1.7kg/mm/m2 7、Construction technology 7.1 The steel deck need be rust-protect treatment,it is no oil pollution,dust and other contaminants on the surface. 7.2 Mix stirring evenly the interface agent and water according to the 5:1,brush or roller uniform on the steel deck; 7.3 After the interface agent curing,mix the AC - JIII self-leveling deck covering and water according to the 1:0.175,use hand blender or pumping machine (suggest using pumping machine) laying the AC - JIII self-leveling deck covering on the steel deck; 7.4 Control the thickness of the deck covering with a serrated scraper ; 7.5 Use a foam roller to remove the air bubbles in the deck covering, and promote the flow of the deck covering. 7.6 After construction of deck covering must be curing 12 hours, after basic dry can walk on it; 8、Note 8.1 After mixing,the deck covering must be finished laying within one hour, if manually stirring must be stirring evenly. 8.2 During the deck covering construction and curing, the environmental temperature should be in 10 ~ 35 ° C.When the temperature above 35 ℃ cooling measures should be taken;When the temperature lower 0 ℃ heat preservation measures should be taken. 8.3 The deck covering should be moistureproof, prevent bask in, and stored in a ventilation environment.Material shelf life is 6 months.

Features: This product is non-toxic, strong adhesion, low thermal conductivity, good liquidity, impact resistant, wear resistant, products forming smooth,sound insulation is strong, curing time steady, etc.Its construction technology is simple and apply to the A60 refractory deck area of the vessel .

Fire rating: Noninflammability: comply with IMO 2010 FTP Code Part 1

Parameter DNV.GL、CCS、EC

颜色：

注意事项：

Order online

Details
Precautions
Features

1、Type of construction

Use for the A-60 deck system(see A-60 deck specification)

2、Technical Index

Serial Number	Project Name	Technical Index
1	Dry Density	≤1700kg/m3
1	Density	≤1900kg/m3
2	· Fluidity	Φ≥130mm
3	Breaking Strength	≥3.5MPa
4	Compressive Strength	≥10MPa
5	· Water Absorption	≤10％
6	· oil absorption	≤5%
7	Heat Conductivity Coefficient	≤1.2W/(m.K)
8	Impact Resistance	No crack, no shell
9	Initial Setting Time	≥1h
10	· Final Setting Time	≤8h
11	Vibratory Test	No crack, no shell
12	Organic Content	≤10％
13	Noninflammability	Comply with IMO 2010 FTP Code Part 1

3、The performance characteristics

This product is non-toxic, strong adhesion, low thermal conductivity, good liquidity, impact resistant, wear resistant, products forming smooth,sound insulation is strong, curing time steady, etc.Its construction technology is simple and apply to the A60 refractory deck area of the vessel .

4、Fire resistance rating

Noninflammability: comply with IMO 2010 FTP Code Part 1.

5、Recognised classification society

DNV.GL、CCS、EC

6、Packaging and dosage

Package:25KG/bag 40bags/pallet

Dosage:1.7kg/mm/m2

7、Construction technology

7.1 The steel deck need be rust-protect treatment,it is no oil pollution,dust and other contaminants on the surface.

7.2 Mix stirring evenly the interface agent and water according to the 5:1,brush or roller uniform on the steel deck;

7.3 After the interface agent curing,mix the AC - JIII self-leveling deck covering and water according to the 1:0.175,use hand blender or pumping machine (suggest using pumping machine) laying the AC - JIII self-leveling deck covering on the steel deck;

7.4 Control the thickness of the deck covering with a serrated scraper ;

7.5 Use a foam roller to remove the air bubbles in the deck covering, and promote the flow of the deck covering.

7.6 After construction of deck covering must be curing 12 hours, after basic dry can walk on it;

8、Note

8.1 After mixing,the deck covering must be finished laying within one hour, if manually stirring must be stirring evenly.

8.2 During the deck covering construction and curing, the environmental temperature should be in 10 ~ 35 ° C.When the temperature above 35 ℃ cooling measures should be taken;When the temperature lower 0 ℃ heat preservation measures should be taken.

8.3 The deck covering should be moistureproof, prevent bask in, and stored in a ventilation environment.Material shelf life is 6 months.